PLEXIGLAS® Mineral - 3D thermoformable

Physical characteristics - values at 23°C and 50% RH

Mechanical properties
	Values	Measurement unit	Test regulation
Flexural modulus of elasticity	min. 4700	MPa	ISO 178
Bending strength	80	MPa	ISO 178
Elongation at break	2,1	%	ISO 527-2/1B/5
Tensile strength	min. 42	MPa	ISO 527-2/1B/5
Resistance to impact by large diameter ball	> 1800	mm	EN 483-2
Apparent density	1,5	g/cm³	ISO 1183
Area weight	12 at 8 mm	kg/m²	-
Module of elasticity	min. 4800	MPa	ISO 527-2/1B/5
Charpy impact strength	1,1	kJ/m²	ISO 179/1eA
Abrasion resistance by Taber Abraser	145 - 160	mg	DIN 14688/2006
Hardness - Barcol	50 - 70		DIN EN 59
Thickness tolerance	conform		prISO 19712
Anti-slip-property	class C		DIN 51097
Fire class	B 2		DIN 4102 Part 1

Thermal properties
	Values	Measurement unit	Test regulation
Thermical coefficient of elongation	50 x 10⁶	1/K	DIN 53752-A
Heat-Deflection-Temperature (HDT)	104 - 108	°C	ISO 75
Vicat temperature process B	> 112	°C	ISO 306/B50
Thermoforming temperature	180 - 215	°C
Min. bending radius	2 x	thickness of the sheet
Thermal shock resistance	no failure		prEN 14688:2003 prISO 19712